dc.contributor.authorK., Ramly,-
dc.contributor.authorA. S. A., Khiar,-
dc.contributor.authorM. I. N., Isa,-
dc.description.abstractPolymer blending is used to overcome the disadvantage of pure starch film, and in the present study, starch has been blended with poly(ethylene oxide) (PEO). The X-ray diffraction study shows that starch/PEO with a ratio of 7 : 3 exhibits the least amount of crystallinity, and this was chosen in the preparation of polymer electrolyte. Films of starch/PEO blends were then prepared via solution casting technique, and their properties with different amounts of ammonium nitrate NH4NO3 were compared. The highest conductivity at room temperature of similar to 2.81 +/- 0.46 x 10(7) S cm(-1) was achieved with the addition of 35 wt-% NH4NO3. Dielectric data were analysed using complex permittivity and complex electrical modulus for the sample with the highest ionic conductivity. The relaxation time tau for these samples was determined, and the plot shows that tau decreases with conductivity of the complexes. The presence of peaks in the imaginary plots shows that the starch/PEO electrolyte system is an ionic conductor.en_US
dc.publisherManey Publishingen_US
dc.subjectPolymer Blendingen_US
dc.titleConductivity and dielectric behaviour studies of starch/PEO plus x wt-% NH4NO3 polymer electrolyteen_US
Appears in Collections:Materials Research Innovations

Files in This Item:
File Description SizeFormat 
Conductivity and dielectric behaviour studies.pdf182.33 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.